During the roll casting process of AZ31B alloy , rolling force should not be large , otherwise it will cause heat cracking .

在 AZ31B 合金铸轧过程中，轧制力不能太大，否则容易引起热裂。

3

Summarizes the investigations in press forming of extrusion, rolling and deep drawing in AZ31B wrought magnesium alloy .

总结了 AZ31B 变形镁合金挤压、轧制和热冲压拉深的研究工作。

4

5

In the experiment, die cast magnesium alloy AZ91D and wrought magnesium alloy AZ31B were used as experimental materials .

论文选用 AZ91D 压铸镁合金和 AZ31B 变形镁合金作为实验材料。

6

Based on the wrought AZ31B magnesium alloy , the effect of the welding parameter on weld shape was analyzed in the course of the TIG welding .

以 AZ31 变形镁合金为研究对象，分析了其 TIG 自动焊过程中焊接工艺参数对焊缝成型的影响。

8

There are no pole and crack in welding joint .

AZ31B 镁合金焊接接头没有气孔生成，无热裂纹。

9

While the AZ31B is used , or no filler metal is used, the crack appears in the weld seam .

采用 AZ31B 作为填充材料或直接对焊时，焊缝均有裂纹。